Song, HP;Liu, CC;Zhang, H;Yang, XD;Chen, YJ;Leen, SB
2021
January
Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing
Experimental investigation on damage evolution in pre-corroded aluminum alloy 7075-T7651 under fatigue loading
Published
WOS: 1 ()
Optional Fields
CORROSION-FATIGUE CRACK-GROWTH LOCALIZED CORROSION LIFE PREDICTION BEHAVIOR INITIATION MODEL LIVES
799
This paper experimentally investigates the fatigue damage evolution in pre-corroded aluminum alloy (AA) 7075-T7651 via digital image correlation (DIC) and scanning electron microscopy (SEM). Three stages of fatigue damage evolution including damage accumulation, macro-crack initiation and propagation are identified and described via the combined analysis of damage severity curves and strain maps. The micro-cracking characteristics in the dominant fracture regions are examined by fractography analysis. The experimental results show that localized corrosion penetrated in the 'L-S' or 'L-T' surfaces promotes fatigue crack initiation, affecting crack nucleation location, cracking path, and is accompanied with quasi-cleavage fracture. Damage evolution and failure progression differed temporally and spatially between specimens for the same loading conditions, due to the stochastic diversity of localized corrosion. Multiple corrosion-induced cracks were observed to initiate and evolve under different loading conditions: three typical failure modes, viz. single crack fracture, multi-crack competition and multi-crack parallel growth, were observed to depend on loading condition and relative location of macro-crack initiation.
0921-5093
10.1016/j.msea.2020.140206
Grant Details
Publication Themes